Aluminium Sheet is a lightweight, versatile, and corrosion-resistant material that is ideal for a wide range of industrial and commercial applications. Its excellent strength-to-weight ratio, thermal and electrical conductivity, and non-toxic properties make it suitable for industries such as transportation, packaging, aerospace, and construction. At Kaustubh Enterprises, we offer high-quality aluminium sheets in various grades and sizes to meet your specific needs.

Aluminium sheets are known for their ease of fabrication, recyclability, and sleek appearance. They can be cut, welded, and formed into various shapes, making them perfect for custom fabrication. Our sheets are tested to meet industry standards, ensuring durability and performance even in harsh environments. Trust Kaustubh Enterprises for reliable and precision-supplied aluminium sheet solutions.

AL6065 Chemical Composition
Element Content (%)
Silicon (Si) 0.40 – 0.80
Iron (Fe) ≤ 0.70
Copper (Cu) 0.15 – 0.40
Manganese (Mn) 0.15
Magnesium (Mg) 0.80 – 1.20
Chromium (Cr) ≤ 0.15
Zinc (Zn) ≤ 0.25
Titanium (Ti) ≤ 0.15
Aluminium (Al) Balance
AL6065 Mechanical Properties
Property Value Unit
Tensile Strength 260 – 310 MPa
Yield Strength 240 MPa
Elongation 8 – 12 %
Hardness 95 HB
AL6061 Chemical Composition
Element Content (%)
Magnesium (Mg) 0.80 – 1.20
Silicon (Si) 0.40 – 0.80
Iron (Fe) ≤ 0.70
Copper (Cu) 0.15 – 0.40
Chromium (Cr) 0.04 – 0.35
Zinc (Zn) ≤ 0.25
Titanium (Ti) ≤ 0.15
Other Elements ≤ 0.15
Aluminium (Al) Balance
AL6061 Mechanical Properties
Property Value Unit
Tensile Strength 290 – 310 MPa
Yield Strength 240 MPa
Elongation 10 – 18 %
Hardness 95 HB
AL7075 Chemical Composition
Element Content (%)
Zinc (Zn) 5.1 – 6.1
Magnesium (Mg) 2.1 – 2.9
Copper (Cu) 1.2 – 2.0
Silicon (Si) ≤ 0.40
Iron (Fe) ≤ 0.50
Chromium (Cr) 0.18 – 0.28
Titanium (Ti) ≤ 0.20
Other Elements ≤ 0.15
Aluminium (Al) Balance
AL7075 Mechanical Properties
Property Value Unit
Tensile Strength 510 – 560 MPa
Yield Strength 430 – 480 MPa
Elongation 7 – 11 %
Hardness 150 – 160 HB
AL7050 Chemical Composition
Element Content (%)
Zinc (Zn) 5.7 – 6.7
Magnesium (Mg) 1.9 – 2.6
Copper (Cu) 2.0 – 2.6
Zirconium (Zr) 0.08 – 0.15
Silicon (Si) ≤ 0.12
Iron (Fe) ≤ 0.15
Other Elements ≤ 0.15
Aluminium (Al) Balance
AL7050 Mechanical Properties
Property Value Unit
Tensile Strength 510 – 570 MPa
Yield Strength 455 – 510 MPa
Elongation 8 – 10 %
Hardness 160 – 180 HB
HE14 Chemical Composition
Element Content (%)
Magnesium (Mg) 2.2 – 3.0
Manganese (Mn) 0.3 – 1.0
Iron (Fe) ≤ 0.5
Silicon (Si) ≤ 0.40
Copper (Cu) ≤ 0.1
Chromium (Cr) ≤ 0.1
Aluminium (Al) Balance
HE14 Mechanical Properties
Property Value Unit
Tensile Strength 270 – 320 MPa
Yield Strength ≥ 130 MPa
Elongation 10 – 18 %
Hardness 60 – 80 HB
HE13 Chemical Composition
Element Content (%)
Magnesium (Mg) 2.2 – 3.0
Manganese (Mn) 0.3 – 1.0
Iron (Fe) ≤ 0.5
Silicon (Si) ≤ 0.4
Copper (Cu) ≤ 0.1
Chromium (Cr) ≤ 0.1
Aluminium (Al) Balance
HE13 Mechanical Properties
Property Value Unit
Tensile Strength 240 – 300 MPa
Yield Strength ≥ 130 MPa
Elongation 8 – 15 %
Hardness 55 – 75 HB
AL 1100 Chemical Composition
Element Content (%)
Aluminium (Al) ≥ 99.00
Copper (Cu) 0.05 – 0.20
Iron (Fe) ≤ 0.35
Silicon (Si) ≤ 0.95 (Si + Fe)
Zinc (Zn) ≤ 0.10
Manganese (Mn) ≤ 0.05
Others (Each) ≤ 0.05
Others (Total) ≤ 0.15
AL 1100 Mechanical Properties
Property Value Unit
Tensile Strength 90 – 130 MPa
Yield Strength 35 – 75 MPa
Elongation 10 – 35 %
Hardness (Brinell) 20 – 35 HB
AL 1200 Chemical Composition
Element Content (%)
Aluminium (Al) ≥ 99.00
Silicon + Iron (Si + Fe) ≤ 0.60
Copper (Cu) ≤ 0.05
Manganese (Mn) ≤ 0.05
Magnesium (Mg) ≤ 0.05
Zinc (Zn) ≤ 0.10
Others (Each) ≤ 0.03
Others (Total) ≤ 0.10
AL 1200 Mechanical Properties
Property Value Unit
Tensile Strength 60 – 110 MPa
Yield Strength 30 – 65 MPa
Elongation 20 – 35 %
Hardness (Brinell) 20 – 30 HB
AL 8011 Chemical Composition
Element Content (%)
Aluminium (Al) 97.3 – 98.9
Iron (Fe) 0.60 – 1.00
Silicon (Si) 0.50 – 0.90
Manganese (Mn) ≤ 0.20
Zinc (Zn) ≤ 0.10
Copper (Cu) ≤ 0.10
Magnesium (Mg) ≤ 0.05
Titanium (Ti) ≤ 0.080
Chromium (Cr) ≤ 0.050
Others (each) ≤ 0.05; total ≤ 0.15
AL 8011 Mechanical Properties
Property Typical Range Unit
Tensile Strength (UTS) 100 – 180 MPa
Yield Strength 34 – 170 MPa
Elongation at Break 1.7 – 28 %
Hardness (Brinell) 25 – 50 HB
AL 6063 Chemical Composition
Element Content (%)
Magnesium (Mg) 0.45–0.90
Silicon (Si) 0.20–0.60
Iron (Fe) ≤ 0.35
Copper (Cu) ≤ 0.10
Manganese (Mn) ≤ 0.10
Chromium (Cr) ≤ 0.10
Titanium (Ti) ≤ 0.10
Zinc (Zn) ≤ 0.10
Other elements (each) ≤ 0.05, total ≤ 0.15
Aluminium (Al) Balance
AL 6063 Mechanical Properties (T6 temper typical)
Property Value Unit
Tensile Strength (UTS) ~215 MPa
Yield Strength (Proof Stress) ~170 MPa
Elongation ≥ 8 (≈10 for thicker sections) %
Hardness (Brinell) ~75 HB
AL 6063 Chemical Composition
Element Content (%)
Magnesium (Mg) 0.45–0.90
Silicon (Si) 0.20–0.60
Iron (Fe) ≤ 0.35
Copper (Cu) ≤ 0.10
Manganese (Mn) ≤ 0.10
Chromium (Cr) ≤ 0.10
Titanium (Ti) ≤ 0.10
Zinc (Zn) ≤ 0.10
Other elements (each) ≤ 0.05, total ≤ 0.15
Aluminium (Al) Balance
AL 6063 Mechanical Properties (T6 temper typical)
Property Value Unit
Tensile Strength (UTS) ~215 MPa
Yield Strength (Proof Stress) ~170 MPa
Elongation ≥ 8 (≈10 for thicker sections) %
Hardness (Brinell) ~75 HB
AL 5051 Chemical Composition
Element Content (%)
Magnesium (Mg) 2.2 – 2.8
Silicon (Si) ≤ 0.40
Iron (Fe) ≤ 0.40
Copper (Cu) ≤ 0.10
Manganese (Mn) ≤ 0.10
Chromium (Cr) 0.15 – 0.35
Zinc (Zn) ≤ 0.25
Titanium (Ti) ≤ 0.15
Other (each) ≤ 0.05, total ≤ 0.15
Aluminium (Al) Balance
AL 5051 Mechanical Properties
Property Typical Value Unit
Tensile Strength (UTS) 175 – 260 MPa
Yield Strength 80 – 200 MPa
Elongation 12 – 25 %
Hardness (Brinell) 50 – 65 HB
AL 5052 Chemical Composition
Element Content (%)
Magnesium (Mg) 2.2 – 2.8
Silicon (Si) ≤ 0.25
Iron (Fe) ≤ 0.40
Copper (Cu) ≤ 0.10
Manganese (Mn) ≤ 0.10
Chromium (Cr) 0.15 – 0.35
Zinc (Zn) ≤ 0.10
Titanium (Ti) ≤ 0.15
Other (each) ≤ 0.05, total ≤ 0.15
Aluminium (Al) Balance
AL 5052 Mechanical Properties
Property Typical Value Unit
Tensile Strength (UTS) 210 – 280 MPa
Yield Strength 130 – 240 MPa
Elongation 7 – 25 %
Hardness (Brinell) 60 – 80 HB